Brass bars 2.0401 non-ferrous metal Ms 58 brass non-ferrous metal CW614N 25gr-5kg
- Wnr. 2.0401; EN CuZn39Pb3;
- Fields of application: fittings & water tap handles; threaded rods, cable clamps, screws, nuts; printed circuit boards & pin headers; clock parts; ballpoint pen tips; parts for electrical engineering and general mechanical engineering;
- Properties: good hot formability and very good machinability; low corrosion resistance; diamagnetic; very well suited for soft soldering and galvanizing; not very weldable; suitable for machining on automatic machines;
- Density 8.47 g/cm³; melting point 888 °C; tensile strength min. 360 MPa;
- Thermal conductivity 123 W/m·K; electrical conductivity 15 m/Ω•mm²; electrical resistance 0.066 Ω•mm²/m.
Length tolerance +/-2mm
Do you need a different steel grade or dimensions? Please write to us. Our sales team will make you an offer from our stock program or delivery program :)
- Production time - 5-7 weeks;
- Shipping preparation - 2-3 working days;
- Delivery time - depending on the parcel service. Please check the FAQ.
Copper (about 57-59 %), lead (approx. 2.5-3.5 %), and zinc (approximately 36-40 %) are the main components of the offered brass bars. The material also contains nickel, iron, tin, aluminum, and other minor constituents. The material is characterized by good hot formability, very good machinability, and low corrosion resistance against water and various salt solutions. Normally 2.0401 is diamagnetic. The grade can be very well soft-soldered and galvanized. In addition, CuZn39Pb3 is well suited for machining on automatic machines and in a tin bath (dip tinning). The material is not recommended for welding: however, if welding is required, resistance welding is best to recommend.
You can buy brass bars in the Evek GmbH online shop. We offer non-ferrous metal alloys at a good price.
2.0401 has the following applications:
- Fittings & water tap handles;
- Threaded rods, cable clamps, screws, nuts;
- Printed circuit boards & pin headers;
- Clock parts;
- Ballpoint pen tips;
- Parts for electrical engineering and general mechanical engineering.
CuZn39Pb3 has the following properties:
- good hot formability and very good machinability;
- low corrosion resistance;
- diamagnetic;
- very well suited for soft soldering and galvanizing;
- not very weldable;
- suitable for machining on automatic machines.
Chemical composition (in %)
| Cu | Zn | Pb | Ni | Fe | Sn | Al | Other |
| 57.0 - 59.0 | Balance | 2.5 - 3.5 | 0.3 | 0.5 | 0.3 | 0.05 | 0.2 |