Brass hexagon with the material number 2.0401 is made from a copper-zinc-lead alloy. The copper content is around 57-59%, zinc - 36-40% and lead - 2.5-3.5%. CuZn39Pb3 is the main alloy for machining in Germany. The material is particularly suitable for processing on automatic machines. Hexagonal brass is also easy to punch, but at the same time has low corrosion resistance. The material can be hot-formed very well and cold-formed only to a limited extent (because of the risk of stress corrosion cracking). High hardness and strength are achieved through cold formability.
Buy hexagonal brass 2.0401 Ms58 in the Evek GmbH online shop. We take care of it so that you remain satisfied with our service and our products.
Brass hexagon has very good machinability and is easy to soft and hard solder. Resistance welding is the most recommended for welding 2.0401. Other welding processes should be avoided. 6-point brass is easy to mechanically polish and very easy to electroplate.
Hexagonal brass with the designation CuZn39Pb3 Ms58 is widely used in different fields. How to make from this material:
- faucet handles;
- parts for electrical engineering;
- building profiles;
- various turned parts.
Material 2.0401 is characterized by the following features:
- very good machinability;
- good hot workability;
- easy to stamp, polish and electroplate;
- low corrosion resistance;
- suitable for automatic processing;
- easy to soft and hard solder.
Evek GmbH as a reliable supplier offers brass 2.0401 at a good price. We ship internationally and are happy to answer any questions you may have.
Chemical composition (in %)
| Cu|| Zn|| pb|| no|| feet|| sn|| Al|| Other|
| 57.0 - 59.0|| rest|| 2.5 - 3.5|| 0.3|| 0.5|| 0.3|| 0.05|| 0.2|